依凡坦40-55是由乙烯和醋酸乙烯经高压自由基聚合而成的无规共聚物。高醋酸乙烯酯含量的Evatane 40-55具有柔软性、柔韧性、极性和高溶解性。Evatane 40-55与大多数增粘树脂和蜡兼容。结合高流动性,它是一个高效和容易处理的产品热熔胶配方。Evatane 40-55也可用于溶剂型粘合剂、油墨配方和制造泡沫(制鞋工业)。 EVATANE? 40-55 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE? 40-55 brings softness, flexibility, polarity and high solubility. EVATANE? 40-55 is compatible with most tackifying resins and waxes. Combined with a high fluidity, it is an efficient and easy handling product for hot melt adhesives formulations. EVATANE? 40-55 can also be used in solvent base adhesives, inks formulation and for making foams (shoe industry).

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:EVA EVA 用途:印刷油墨;泡沫;粘合剂; 性能特点: 柔软性好; 无规共聚物; 流动性高; 韧性好; Good flexibility,High liquidity,Random copolymer,Soft
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Density (73°F) g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃, 190℃/ kg 48 to 62 g/10min ASTM D1238
190℃, 190℃/ kg 48 to 62 g/10min ISO 1133
醋酸乙烯含量 Vinyl Acetate Content to wt% Internal Method
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
邵氏硬度 邵氏硬度
邵氏 A 邵氏 A 50 ISO 868
邵氏 A 邵氏 A 50 ASTM D2240
拉伸强度 拉伸强度
断裂 断裂 MPa ASTM D638
断裂 断裂 MPa ISO 527-2
拉伸应变 拉伸应变
断裂 断裂 900 to 1100 % ASTM D638
断裂 断裂 900 to 1100 % ISO 527-2
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature < ℃ ASTM D1525 2
维卡软化温度 Vicat Softening Temperature < ℃ ISO 306/A
熔融温度 Melting Temperature ℃ ISO 11357-3
Ring and Ball Softening Point Ring and Ball Softening Point 3 3 97 ℃ ASTM E28
备注
1 一般属性:这些不能被视为规格。
2 压 力1 (10N)
3 NF EN 1238