牌号简介 About
OREVAC 18334是一种顺丁烯二酸酐改性线性低密度聚乙烯,以颗粒形式提供。它可以在大多数设计用于加工传统聚烯烃的挤压设备上进行加工。应用OREVAC 18334设计用于在共挤过程中开发聚乙烯或乙烯共聚物与极性树脂(如聚酰胺和EVOH)之间的可靠粘合强度。OREVAC 18334建议用于吹塑或管共挤。OREVAC 18334可作为三层管道涂层的粘合剂。 OREVAC? 18334 is a maleic anhydride modified linear low-density polyethylene available in pellet form. It can be processed on most extrusion equipment designed to process conventional polyolefins. Applications OREVAC? 18334 has been designed to develop a reliable bonding strength between polyethylene or ethylene copolymers and polar resins such as polyamides and EVOH within a coextrusion process. OREVAC? 18334 is recommended for blow moulding or tube coextrusion. OREVAC? 18334 can be used as the adhesive for three layers pipe coating.

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:LLDPE Linear low density polyethylene 用途:管线涂料;吹塑成型应用;粘合剂; 加工条件:挤出 Extrusion 性能特点: 抗氧化; 粘结性好; 易加工; Excellent Processability,Good bond,Inoxidizability
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Density g/cm3 ASTM D1505
密度 Density g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃, 190℃/ kg g/10min ISO 1133
190℃, 190℃/ kg g/10min ASTM D1238
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
拉伸强度 拉伸强度
断裂,模压成型 断裂,模压成型 MPa ASTM D638
断裂,模压成型 断裂,模压成型 MPa ISO 527-2
屈服,模压成型 屈服,模压成型 MPa ISO 527-2
屈服,模压成型 屈服,模压成型 MPa ASTM D638
拉伸应变 拉伸应变
断裂,模压成型 断裂,模压成型 700 % ASTM D638
断裂,模压成型 断裂,模压成型 700 % ISO 527-2
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature 101 ℃ ASTM D1525
维卡软化温度 Vicat Softening Temperature 101 ℃ ISO 306
熔融温度 Melting Temperature 125 ℃ ISO 11357-3